High Performance Piperzine Pyrophosphate Flame Retardant for Polypropylene

• Customization: Available
• CAS No.: 66034- 17- 1
• Formula: /
• Model NO.: Mflam 1430
• EINECS: /
• Certification: REACH, RoHS
• Environmental Protection: Yes
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Powder
• Application: PP-GF, PP, PE
• Flame Class: UL94_V0
• Recommend Process Condition ºC: Less Than 210 Degrees Celsius
• The Content of Phosphorus: 16%-20%
• The Content of Nitrogen: 18%-22%
• Transport Package: 25kg Paper Bag, 17.5mt/20′fcl
• Specification: Piperazine Pyrophosphate
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: 8000mt/Year

Product Description

                        Halogen Free Flame Retardant for Pure PP PP+GF-30, for EV Car battery case final application

Specification:

 

Item	Index
Appearance	White Powder
The Content of Phosphorus %(W/W)	18±2
The Content of Nitrogen %(W/W)	20±2
Particle Size D50 (μm)            D90(um)	5±3 15±4
Moisture   %(W/W)	≤0.5
TGA (20ºC/min, in N2)	Weight Loss 1%	≥250ºC
	Weight Loss 5%	≥290ºC
Recommend Process Condition ºC	≤ 210

 

Application:

Mflam 1430 is a halogen-free intumescent flame retardant for polyolefins, especially for PP glass fiber reinforced. PP treated by Mflam 1430, can reach UL 94 V-0 (0.8mm), and pass the 70 °C X168 hours water immersion test (UL746C), while passing GWIT 900 ° C and GWFI 960 ° C glow wire test. Mflam 1430 can also be applied to glass fiber reinforced PP, can reach UL 94 V-0 (0.8mm).

In TPE application, Mflam 1430 is also a very good choice.
 

Our Advantages

Mflam 1430 is especially for glass fiber reinforce PP, and the PP which have the high requirement of high temperature and water solubility.

Another advantage of Mflam 1430 is: the PP made by Mflam 1430 can replace of PC/ABS engine plastic, same function, lower cost.
 

Dosage:

 

Polymer	pp	PE
Mflam 1430  Dosage%	3.2mm: 15-20% 1.6mm: 22-25% 0.8mm: 22-30%	3.2mm: 18-23% 1.6mm: 23-28% 0.8mm: 25-33%
Flame Retardancy	UL 94 V-0, 5VA

PS: it can be added 10-30% glass fiber in PP.



Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.

Remarks:
(1) The initial thermal decomposition temperature of Mflam 1430 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mflam 1430 is used in PP, it is not recommended to use a combination of strong shear screws.