Nylon Melamine Cyanurate Fr Masterbatch for PA6, PA66, with PA Resin as The Carrier

• Customization: Available
• CAS No.: 37640-57-6
• Appearance: Granules
• Model NO.: Mflam MB MC
• Usage: Plastic Auxiliary Agents
• Color: White
• Mca Content: More Than 50%
• Melting Index G/10min: 15-25
• Volatile: Less Than 0.5
• Carrier: PA6
• Transport Package: 25kg Paper Bag, 17.5mt/20′fcl
• Specification: Melamine Cyanurate
• Trademark: Mflam
• Origin: China
• HS Code: 2933699099
• Production Capacity: 10000mt/Year

Product Description

Nylon Melamine Cyanurate FR Masterbatch for PA6, PA66, with PA resin as the carrier

This product is a functional masterbatch of MCA with PA6 resin as the carrier. It is mainly used in nitrogen-based halogen-free flame-retardant nylon system to give nylon products high-efficiency and stable flame-retardant properties.

Specification

 

Item	Unit	Standard
Appearance		White granule
MCA content	%	50±0.5
Melting index(230ºC/5kg)	g/10min	20±5
Volatile(105ºC/2hr)	%	≤0.5
Carrier		PA6

Feature
1. Compared with powder MCA, it has higher dispersion, and the flame retardant grade and mechanical properties (especially toughness) of the obtained product are more stable.
2. Meet dust-free requirements, easy to transport and mix, can greatly improve the stability of weighing and granulation, and avoid product quality fluctuations.

Recommend dosage

This product is directly mixed with materials in proportion to use, and the effect of extruding and granulating through a twin-screw extruder is the best.
 

FR	PA66 0.8mm V-0	PA6 0.8mm V-0	Remarks
Mflam MB MC	18-22%	22-26%	1.8:1 replace  MCA powder

Remarks

Before granulation and injection molding, the equipment must be carefully cleaned to avoid impurities that affect the flame retardant effect. In addition, the MCA masterbatch has been added with related additives, and there is no need to add antioxidants and lubricants separately during granulation to prevent these additives from adversely affecting the flame retardant effect. For the black masterbatch, it is recommended to use the organic black of the PA carrier.
to prevent the carrier resin in the carbon black masterbatch from affecting the flame retardancy of the MCA system.

Package and stock

25Kg/bag; Please place it in a dry and ventilated place, away from moisture and direct sunlight.

 

Application example

Mflam MC15 for PA66/6
 

Raw material		PA6	PA66
PA6		76	-
PA66		-	80
Mflam MB MC		24	20
Item	Test standard	Result
Tensile Strength,MPa	GB/T 1040-02	69	71
Bending strength,MPa	GB/T 9314-00	95	105
Impact strength of simply supported beam (notch),KJ/m2	GB/T 1043.1-2008	5.5	4.5
Impact strength of simply supported beam (non-notched),KJ/m2	GB/T 1043.1-2008	105	69
HDT(1.82MPa),ºC	GB/T1634.1-04	60	68
Anti-flammability(0.8mm)	UL-94	V-0	V-0

Remarks: The above data is for reference only, the specific addition amount depends on the actual demand, you can consult the technical engineer of our company.