| Customization: | Available |
|---|---|
| CAS No.: | 66034- 17- 1 |
| Formula: | / |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
High efficient flame retardancy flame retardant for GF-PP, PP, PE Olefinic polymers Passing GWIT
| Item | Index | |
| Appearance | White Powder | |
| The Content of Phosphorus %(W/W) | 18±2 | |
| The Content of Nitrogen %(W/W) | 20±2 | |
| Particle Size D50 (μm) D90(um) |
5±3 15±4 |
|
| Recommend Process Condition ºC | ≤ 250 | |
| Moisture %(W/W) | ≤0.5 | |
| TGA | Weight Loss 1% | ≥250ºC |
| (10ºC/min, in N2) | Weight Loss 5% | ≥290ºC |
Mflam 1530 is a halogen-free intumescent flame retardant for polyolefins, especially for PP glass fiber reinforced. PP treated by Mflam 1430, can reach UL 94 V-0 (0.8mm), and pass the 70 °C X 168 hours water immersion test (UL746C), while passing GWIT 900 ° C and GWFI 960 ° C glow wire test. Mflam 1530 can also be applied to glass fiber reinforced PP, can reach UL 94 V-0 (0.8mm).
In TPE application, Mflam 1530 is also a very good choice.Mflam 1530 is especially for glass fiber reinforce PP, and the PP which have the high requirement of high temperature and water solubility.
Another advantage of Mflam 1430 is: the PP made by Mflam 1530 can replace of PC/ABS engine plastic, same function, lower cost.| Polymer | pp | PE |
| Mflam 1530 Dosage% |
3.2mm: 15-20% 1.6mm: 22-25% 0.8mm: 22-30% |
3.2mm: 18-23% 1.6mm: 23-28% 0.8mm: 25-33% |
| Flame Retardancy | UL 94 V-0, 5VA | |
PS: it can be added 10-30% fiber glass in PP.
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.
(1) The initial thermal decomposition temperature of Mflam 1430 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mflam 1430 is used in PP, it is not recommended to use a combination of strong shear screws.