Polyamide High Efficient Flame Retardant for 30% Glass Fiber Reinforced PA and PBT

• Customization: Available
• CAS No.: 225789-38-8
• Environmental Protection: Yes
• Model NO.: Mflam HC-16
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Powder
• Application: PA6, PA66, PBT
• Flame Class: UL94 V0
• Particle Size D50: 17-27 Micron
• Process Condition: Less Than or Equal to 245 Degrees Celsius
• Transport Package: 20kg Paper Bag, 14mt/20′fcl
• Specification: Aluminum Diethyl Phosphinate
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: 5000mt/Year

Product Description

Polyamide high efficient flame retardant for 30% glass fiber reinforced PA and PBT

Introduction
Mflam HC-16 is organic phosphinates based flame retardant especially for PA6, PA66, PBT, etc. It higher grade, which has high flame retardant efficiency, good thermal stability, no immigration, excellent water resistance, good aging resistance and low smoke non-toxicity.

Specification:

Item	Index
Appearance	White Powder
The Content of Phosphorus %(W/W)	22±2
The Content of Nitrogen %(W/W)	6±2
Particle Size D50 (μm)            D90 (μm)	22±5 55±7
Moisture   %(W/W)	≤0.5
Process condition ºC	≤245
TGA   (20ºC/min, in N2)	Weight Loss 1%	≥320ºC
	Weight Loss 5%	≥360ºC

Recommended dosage:

Material	Glass fiber	Dosage %	Standard	FR level
PA	0-30%	12-14	UL94	V-0(1.6mm)
PBT	0-30%	12-14	UL94	V-0(1.6mm)

Remarks:
The initial thermal decomposition temperature of Mflam HC-16 is about 360 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.

Process:
Screw: twin-screw extrusion 35                 
Temperature (ºC): 240-280
Main engine Speed: 240-360rpm

Shipping Information:
20KG paper bag, 14mt/20'FCL or on customer's request.