| Customization: | Available |
|---|---|
| CAS No.: | 68333-79-9 |
| Formula: | / |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Ammonium Polyphosphate Based Halogen Free Flame Retardant for PP Material to Get UL94-V0
| Item | Index |
| Appearance | White Powder |
| The Content of Phosphorus %(W/W) | 25±2 |
| The Content of Nitrogen %(W/W) | 20±2 |
| Particle Size D50 (μm) D90 (um) |
9±3 23±4 |
| TGA (20ºC/min, in N2) | Weight Loss 1%:≥220ºC |
| Weight Loss 5%: ≥290ºC | |
| Recommend Process Condition ºC | ≤ 190 |
| Moisture %(W/W) | ≤0.5 |
Mflam TC100 is a halogen-free intumescent flame retardant designed by our company for polyolefins with phosphorus and nitrogen as the main flame retardant elements; it mainly plays a flame retardant role in the formation of carbon and expansion flame retardant. It has high flame retardant efficiency, good thermal stability, no precipitation, good water resistance, light aging resistance and low smoke and non-toxicity. PP treated by Mflam TC100 (adding 25%-28%) can reach UL 94 V-0 (1.6mm). Mflam TC100 can also be used in glass fiber reinforced PP, and can reach UL 94 V-0 (0.8mm).
| Polymer | PP | PP+GF(10%) | PP+GF(20%) | PP+GF(30%) | PP+talcum powder (20%) |
| Mflam TC100 dosage % | 25-30 | ≥25 | ≥25 | ≥25 | 24-26 |
| Flame Retardancy | V-0(1.6mm) | V-0(1.6mm) | V-0(0.8mm) | V-0(1.6mm) | V-0(3.2mm) |
| Polymer | PE | ||
| Mflam TC100 dosage % | Cannot do | 33-36 | 30-32 |
| Flame Retardancy | V-0(0.8mm) | V-0(1.6mm) | V-0(3.2mm) |
The package is 25kg craft paper bag or on customer's request, and can be loaded 20mt with pallet in 1x 20'FCL.
(1) The initial thermal decomposition temperature of Mflam TC100 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mlam TC100 is used in PP, it is not recommended to use a combination of strong shear screws.