Environmental Flame Retardant Paste for Coating Polypropylene to Achieve BS5852

• Customization: Available
• Application: Fiber & Garment
• Bonding Function: Flame Retardant Adhesive
• Model NO.: Mflam 6807T
• Color: White
• Composition: Polyacrylate, Dbdpe, ATO
• Morphology: Water Emulsion
• Fabric: Polypropylene
• Flame Class: BS5852
• Finish Method: Back Coating
• Solid Content: 53-55
• Material: Acrylic
• Classification: Thermosetting
• Main Agent Composition: Thermosetting Resin
• CAS No.: 30698-92-1
• Formula: C14h24o4
• Characteristic: Fireproof
• Promoter Composition: Flame Retardant
• Transport Package: 140kg Drum
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999

Product Description

Mflam 6807T
Water-Based Environmental Flame Retardant Paste for Coating Polypropylene to Achieve BS5852


Main component: Polyacrylate composite with flame retardant additives

Specifications

Appearance	Milky white viscous liquid
Solid content (%)	53.0-55.0
pH value (1% aqueous solution)	7.5-9.5
Viscosity (mPa.s, 25ºC)	1000-1500

Performance and Features
1. After reaching a certain weight gain on the polypropylene fabric, the flame retardant effect is excellent, and it is especially suitable for BS-5852 flame retardant test.
2. The treated fabrics are medium soft and dry.
3. It can be coated directly according to the color of the fabric or after adding water- based color paste.
4. Excellent washing resistance.
5. Strict control on polybrominated diphenyl ethers and eight major heavy metals.

Scope of application
Flame retardant coating finishing of polypropylene fabric and polyester blended fabric. 
Recommendation dosage: 90-130g/m2 dry weight

Instructions
Process flow: base fabric→coating→drying (temperature 130ºC/140-160ºC).
Please  select the number  of coats  according to the  fabric  specification  and  flame retardant requirements.

Packaging and Storage
140 kg/plastic drum, 14mt/20FCL, the storage period is 6 months at room temperature.
Note: There is a slight layering phenomenon during storage, and it must be stirred evenly before using.