| Customization: | Available |
|---|---|
| CAS No.: | 225789-38-8 |
| Formula: | C12h30alo6p3 |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Economic Low Cost Flame Retardant for 30% Glass Fiber Reinforced PA6, PA66 Resins
Introduction
Mflam LX-15 is a halogen free flame retardant designed by our company for PA6, PA66, with phosphorus and nitrogen as the main flame retardant elements. It has high flame retardant efficiency, good thermal stability, no immigration, excellent water resistance, good aging resistance and low smoke non-toxicity.
Specification:
| Item | Index | |
| Appearance | White Powder | |
| The Content of Phosphorus %(W/W) | 18±2 | |
| The Content of Nitrogen %(W/W) | 25±2 | |
| Particle Size D50 (μm) D90 (μm) |
9±3 35±5 |
|
| Moisture %(W/W) | ≤0.5 | |
| Process condition ºC | ≤245 | |
| TGA (20ºC/min, in N2) |
Weight Loss 1% | ≥280ºC |
| Weight Loss 5% | ≥360ºC | |
| Material | Glass fiber | Dosage % | Standard | FR level |
| PA6 | 0-30% | 16-18 | UL94 | V-0(1.6mm) |
| PA66 | 0-30% | 16-18 | UL94 | V-0(1.6mm) |
Remarks:
The initial thermal decomposition temperature of Mflam LX-15 is about 360 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
Process:
Screw: twin-screw extrusion 35
Temperature (ºC): 240-280
Main engine Speed: 240-360rpm
Shipping Information:
20KG paper bag, 14mt/20'FCL or on customer's request.