Economic Low Cost Flame Retardant for 30% Glass Fiber Reinforced PA6, PA66 Resins

• Customization: Available
• CAS No.: 225789-38-8
• Environmental Protection: Yes
• Model NO.: Mflam LX-15
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Powder
• Application: Glass Fiber Reinforced PA6, PA66
• Flame Class: UL94 V0
• The Content of Phosphorus: 16%-20%
• The Content of Nitrogen: 23%-27%
• Process Condition: Less Than 245 Degrees Celsius
• Transport Package: 25kg Paper Bag, 12mt/20′fcl, 24mt/40′fcl
• Specification: Aluminum Diethyl Phosphinate
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: 5000mt/Year

Product Description

Economic Low Cost Flame Retardant for 30% Glass Fiber Reinforced PA6, PA66 Resins

Introduction
Mflam LX-15 is a halogen free flame retardant designed by our company for PA6, PA66, with phosphorus and nitrogen as the main flame retardant elements. It has high flame retardant efficiency, good thermal stability, no immigration, excellent water resistance, good aging resistance and low smoke non-toxicity.

Specification:

Item	Index
Appearance	White Powder
The Content of Phosphorus %(W/W)	18±2
The Content of Nitrogen %(W/W)	25±2
Particle Size D50 (μm)            D90 (μm)	9±3 35±5
Moisture   %(W/W)	≤0.5
Process condition ºC	≤245
TGA   (20ºC/min, in N2)	Weight Loss 1%	≥280ºC
	Weight Loss 5%	≥360ºC

Recommended dosage:

Material	Glass fiber	Dosage %	Standard	FR level
PA6	0-30%	16-18	UL94	V-0(1.6mm)
PA66	0-30%	16-18	UL94	V-0(1.6mm)

Remarks:
The initial thermal decomposition temperature of Mflam LX-15 is about 360 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.

Process:
Screw: twin-screw extrusion 35                 
Temperature (ºC): 240-280
Main engine Speed: 240-360rpm