Polyolefin Extrusion Application Use Halogen Free Flame Retardant Additive

• Customization: Available
• CAS No.: 66034- 17- 1
• Certification: REACH, RoHS
• Model NO.: Mflam 1530
• Environmental Protection: Yes
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Powder
• Application: Glass Fiber Reinforce PP, PP
• Flame Class: UL94_V0
• The Content of Phosphorus: 16%-20%
• The Content of Nitrogen: 18%-22%
• Transport Package: 25kg Paper Bag, 17.5mt/20′fcl
• Specification: Piperazine Pyrophosphate
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: 8000mt/Year
• Package Size: 33.00cm * 18.00cm * 10.00cm
• Package Gross Weight: 1.000kg

Product Description

Polyolefin Extrusion Application Use Halogen Free Flame Retardant Additive
 

Specification:
 

Item	Index
Appearance	White Powder
The Content of Phosphorus %(W/W)	18±2
The Content of Nitrogen %(W/W)	20±2
Particle Size D50 (μm)            D90(um)	5±3 15±4
Recommend Process Condition ºC	≤ 250
Moisture   %(W/W)	≤0.5
TGA	Weight Loss 1%	≥250ºC
(10ºC/min, in N2)	Weight Loss 5%	≥290ºC

Application:
Mflam 1530 is a halogen-free intumescent flame retardant for polyolefins, especially for PP glass fiber reinforced. PP treated by Mflam 1430, can reach UL 94 V-0 (0.8mm), and pass the 70 °C X 168 hours water immersion test (UL746C), while passing GWIT 900 ° C and GWFI 960 ° C glow wire test. Mflam 1530 can also be applied to glass fiber reinforced PP, can reach UL 94 V-0 (0.8mm).
In TPE application, Mflam 1530 is also a very good choice.

Advantage:
Mflam 1530 is especially for glass fiber reinforce PP, and the PP which have the high requirement of high temperature and water solubility.
Another advantage of Mflam 1430 is: the PP made by Mflam 1530 can replace of PC/ABS engine plastic, same function, lower cost.

Recommended dosage:

Polymer	pp	PE
Mflam 1530  Dosage%	3.2mm: 15-20% 1.6mm: 22-25% 0.8mm: 22-30%	3.2mm: 18-23% 1.6mm: 23-28% 0.8mm: 25-33%
Flame Retardancy	UL 94 V-0, 5VA

PS: it can be added 10-30% fiber glass in PP.

Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 17.5mt with pallet in 1x 20'FCL.

Remarks:
(1) The initial thermal decomposition temperature of Mflam 1430 in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mflam 1430 is used in PP, it is not recommended to use a combination of strong shear screws.