APP Halogen Free Flame Retardant for Cable and Wire to Pass UL94-V0

• Customization: Available
• CAS No.: 68333-79-9
• Formula: (Nh4po3)N
• Model NO.: Mflam TC100XL
• EINECS: /
• Certification: REACH, RoHS
• Environmental Protection: Yes
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Powder
• Application: Elastomer, TPE/TPV/Tpo
• Flame Class: UL94-V0
• Tga, at 1%: 220 Min
• Tga, at 5%: 290 Min
• Transport Package: 25kg Paper Bag
• Specification: 1*20fcl=20mt
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: /
• Package Size: 20.00cm * 20.00cm * 10.00cm
• Package Gross Weight: 1.500kg

Product Description

Mflam TC100XL

Specification:

Item	Index
Appearance	White Powder
The Content of Phosphorus %(W/W)	25±2
The Content of Nitrogen %(W/W)	20±2
Particle Size D50 (μm)           D90 (um)	9±3 23±4
TGA (20ºC/min, in N2)	Weight Loss 1%:≥220ºC
	Weight Loss 5%: ≥290ºC
Recommend Process Condition ºC	≤ 190
Moisture %(W/W)	≤0.5

Application:
Mflam TC100XL is a halogen-free intumescent flame retardant designed by our company for polyolefins with phosphorus and nitrogen as the main flame retardant elements; it mainly plays a flame retardant role in the formation of carbon and expansion flame retardant. It has high flame retardant efficiency, good thermal stability, no precipitation, good water resistance, light aging resistance and low smoke and non-toxicity. PP treated by Mflam TC100XL (adding 25%-28%) can reach UL 94 V-0 (1.6mm). Mflam TC100XL can also be used in glass fiber reinforced PP, and can reach UL 94 V-0 (0.8mm).

Recommended dosage in plastic:

Polymer	PP	PP+GF (10%)	PP+GF (20%)	PP+GF (30%)	PP+talcum powder (20%)
Mflam TC100XL dosage %	25-30	≥25	≥25	≥25	24-26
Flame Retardancy	V-0(1.6mm)	V-0(1.6mm)	V-0(0.8mm)	V-0(1.6mm)	V-0(3.2mm)

 

Polymer	PE
Mflam TC100XL dosage %	Cannot do	33-36	30-32
Flame Retardancy	V-0(0.8mm)	V-0(1.6mm)	V-0(3.2mm)

Shipping Information:
The package is 25kg craft paper bag or on customer's request, and can be loaded 20mt with pallet in 1x 20'FCL.

Remarks:
(1) The initial thermal decomposition temperature of Mflam TC100XL in air is about 280 °C, so the processing temperature of the twin-screw can be adjusted according to the specific conditions to enhance the dispersion and enhance the plasticization effect. A certain degree of hollowness must be maintained during the twin-screw extrusion process.
(2) When Mlam TC100XL is used in PP, it is not recommended to use a combination of strong shear screws.