Halogen Free Melamine Cyanurate Flame Retardent Masterbatch for Polyamide to Get V0

• Customization: Available
• CAS No.: 37640-57-6
• Formula: /
• Model NO.: Mflam MB MC
• EINECS: 253-575-7
• Certification: REACH, RoHS
• Environmental Protection: Yes
• Color: White
• Kind: Plastic Flame Retardant
• Appearance: Granulars
• Mca Content: 49.5-50.5%
• Carrier: PA6
• Fr Level: UL94 V0 (0.8mm)
• Application: PA6 PA66
• Transport Package: 25kg/Bag
• Specification: 25Kg/bag
• Trademark: Mflam
• Origin: China
• HS Code: 3824999999
• Production Capacity: 50000mt/Year
• Package Size: 64.00cm * 27.00cm * 40.00cm
• Package Gross Weight: 28.000kg

Product Description

Halogen Free Melamine Cyanurate Flame Retardent Masterbatch for Polyamide to Get V0

This product is a functional masterbatch of MCA with PA6 resin as the carrier. It is mainly used in nitrogen-based halogen-free flame-retardant nylon system to give nylon products high-efficiency and stable flame-retardant properties.

Specification:

 

Item	Unit	Standard
Appearance	/	White granule
MCA content	%	50±0.5
Melting index(230ºC/5kg)	g/10min	20±5
Volatile(105ºC/2hr)	%	≤0.5
Carrier	/	PA6

Features:

 

1.  Compared with powder MCA, it has higher dispersion, and the flame retardant grade and mechanical properties (especially toughness) of the obtained product are more stable.
2. Meet dust-free requirements, easy to transport and mix, can greatly improve the stability of weighing and granulation, and avoid product quality fluctuations.

Dosage:

This product is directly mixed with materials in proportion to use, and the effect of extruding and granulating through a twin-screw extruder is the best.

FR	PA66 0.8mm V-0	PA6 0.8mm V-0	Remarks
Mflam MB MC	18-22%	22-26%	1.8:1 replace  MCA powder

Remark:

Before granulation and injection molding, the equipment must be carefully cleaned to avoid impurities that affect the flame retardant effect. In addition, the MCA masterbatch has been added with related additives, and there is no need to add antioxidants and lubricants separately during granulation to prevent these additives from adversely affecting the flame retardant effect. For the black masterbatch, it is recommended to use the organic black of the PA carrier to prevent the carrier resin in the carbon black masterbatch from affecting the flame retardancy of the MCA system.

Packaging & Shipping

25Kg/bag; Please place it in a dry and ventilated place, away from moisture and direct sunlight.

 

Formula reference

 

Raw material		PA6	PA66
PA6		76	-
PA66		-	80
Mflam MB MC		24	20
Item	Test standard	Result
Tensile Strength,MPa	GB/T 1040-02	69	71
Bending strength,MPa	GB/T 9314-00	95	105
Impact strength of simply supported beam (notch),KJ/m2	GB/T 1043.1-2008	5.5	4.5
Impact strength of simply supported beam (non-notched),KJ/m2	GB/T 1043.1-2008	105	69
HDT(1.82MPa),ºC	GB/T1634.1-04	60	68
Anti-flammability(0.8mm)	UL-94	V-0	V-0

Remarks: The above data is for reference only, the specific addition amount depends on the actual demand, you can consult the technical engineer of our company.